Polycrete® ACS


Polyaspartic Fast curing Colored Sealcoat


Product description
Polycrete ACS is a two component, clear aliphatic polyaspartic coating. It provides excellent abrasion resistance, improved scratch resistance and a clear finish.

Fields of application
Polycrete ACS is designed for use as a glossy durable topcoat for Polyaspartic coating systems.

 

Download TDS

Features and benefits

  • Solvent free 

  • Consistent, slightly textured matt finish 

  • Durable 

  • Improves scratch resistance and abrasion resistance 

  • UV-resistant 

  • Good adhesion to non-porous substrates 

  • Low viscosity 

  • Easy to clean and maintain 

  • Very low emissions 


Substrate preparation
The surface to be applied Polycrete ACS must be clean and dry.

Application should be made within 24 hours after installation of the sub layer.

Application
Polycrete ACS is supplied in prepacked units. Before mixing, precondition both A and B components to a temperature of approximately 15 to 20°C. 

Pour the entire contents of part B into the container of part A. Mix with a low speed (ca.300 rpm) electric drill and paddle for at least 3 minutes until homogeneous. Scrape the sides and the bottom of the container several times during mixing to ensure complete mixing. Keep the mixing head submerged to avoid entrapping air. 

Do not work out of the original container. Decant the mixed material into a fresh container and remix for another minute. 

Always work wet-in-wet otherwise you risk getting visible roller marks. 

 Use a max. 40 cm wide short haired roller and start in the middle of one of the short sides of the floor. Dip the roller in the mixed material and apply a strip of Polycrete ACS parallel to the wall next to one of the corners.  Dip the roller in the material again and apply as a path from the starting point and out of the other corner. Go back and repeat these steps while overlapping the first track with a few centimetres. 

 With a new roller scroll backwards without stopping from one corner to the next.  Offset roller with 10 to 20 cm and roll to the opposite wall without stopping. Always roll in same direction to avoid visual differences.

 By using this method, the period between overlaps should not exceed 1-4 minutes, and visible roller marks will be minimized.  Depending on the application method and the consumption,  Polycrete ACS appears with a slightly structured  surface.  This has no influence on the final  properties of the coating. 

The curing time of the material is influenced by the ambient, material and substrate temperatures. At low temperatures, the chemical reactions are slowed down; this lengthens the pot life, open time and curing times. High temperatures speed up the chemical reactions thus the time frames mentioned above are shortened accordingly. To fully cure, the material, substrate and application temperature should not fall below the minimum.

The temperature of the substrate must be at least 3K above the dew point both during the application and for at least 8 hours after application (at 15° C).

Consumption
POLYCRETE ACS: Typically 0.3–0.8 kg/m2. 

Do not exceed the recommended use.

Cleaning agent
Tools must be cleaned immediately after use with Ulfcar® Tool Cleaner or other suitable solvent.

Packaging
Polycrete® ACS is supplied in 8,4 kg, 190 kg or 900 kg units. Polycrete® ACS is used with Polycrete® MC hardener in appropriate quantity.

Shelflife
Minimum 12 months stored in original containers under dry conditions at a temperature between 15-20°C. Do not expose to direct sunlight.


Technical data for Liquid material

PropertyMethodValues
Mixing Ratio A:B 12 kg : 4 kg
Mixed density 1,07 kg/l
Mixed Viscosity@23°CBrookfield DV-II500 cP
Working time@23°C 20 minutes
Ready for traffic@23°C 1 hour
Fully cured 23°C 24 hours
Substrate temperature Min 5°C max 30°C
Max relative humidity Max 85 %

Technical data cured material

PropertyMethodValues
Thickness 0,3-0,8 mm
SHORE D hardnessDIN 5350575
Tensile strengthDIN 53504 
Elongation at BreakDIN 53504>50%
Crack bridging ability >1 mm
Temperature resistance Max 90°C
Water penetration Impervious
Chemical Resistance See separate datasheet
Adhesion to concreteBS/EN 24614>1,5 MPa
Abrasion resistanceEN 1504-265 mg
(Taber)  
Impact resistanceEN 1504-2Class II
Fire classificationEN 1504-2Dfl

This information and all further technical advice is based on our present knowledge and experience. However, it implies no liability or other legal responsibility on our part, including with regard to existing third party intellectual property rights, especially patent rights. In particular, no warranty, whether express or implied, or guarantee of product properties in the legal sense is intended or implied. We reserve the right to make any changes according to the technological progress or further developments. The customer is not released from the obligation to conduct carefull inspection and testing of incoming goods. Performance of the product described herein should be verified by testing, which should be carried out by only qualified experts in the sole responsibility of a customer. Please contact ULFCAR for the latest version. All our documents, offers, ect. are in association with our general sales, delivery and application conditions.

NOUS CONTACTER

Veuillez nous contacter pour toutes questions - nous serons heureux de vous aider.

SIEGE SOCIAL INTERNATIONAL

 Chemin de la Briqueterie 98, 76480 St. Pierre          de Varengeville

 +33 09 54 14 62 53

 contact@atlasol.fr